预形变量对再结晶晶界反常硼偏聚的影响

Effect of Pre-deformation on Abnormal Segregation of Grain Boundary during Recrystallization Process

用二次压缩方法测定了含硼面心Fe-30%Ni合金1000℃热变形10%和40%后保温时的软化率曲线,并由此估计了再结晶过程.用径迹照相方法(PTA)研究了再结晶过程中运动晶界反常偏聚规律以及形变量对反常硼偏聚的影响.用定量统计方法测量了不同形变量下,运动晶界的硼偏聚量.结果表明,新晶粒长大过程中,晶界反常偏聚量与形变量、晶界运动速度等因素有关.并用半定量的方法估算了不同形变量下,再结晶新晶粒长大过程中新晶粒边界向变形晶粒推进时的平均速度.用晶界展宽机制对此现象进行了讨论.

The softening rates of Fe-30%Ni alloy containing boron after 10% and 40% deformation at 1000℃ have been measured by a method of interrupted compression, the recrystallization process has also been evaluated. The moving velocity of the boundary of new recrystallizing grain which was growing into the deformed grains has been calculat- ed semi-quantitatively. By means of PTA technique, the abnormal segregation phenomenon on the moving boundary during recrystallization and the influence of pre-deformation have been investigated and the amount of B segregation on moving grain boundaries has been measured. Results indicate that the abnormal segregation of boundaries, when the new grains are growing, is concerned with the pre-deformation and the moving velocity of the bourdaries. This phenomenon is discussed by the grain boundary widening mechanism.