AlSi_7Mg枝晶合金半固态加热时的组织演变 被引量:4

Microstructral Evolution of the Dendritic AlSi7Mg Alloy during Semi-solid Remelting
下载PDF
导出
摘要 利用电阻炉研究了AlSi_7Mg 枝晶合金半固态加热时的组织演变·研究表明:在(589~597±1)℃下,保温5~120min,初生α枝晶难以完全转化为球状的α相;在较高的半固态加热温度下,若保温时间过长,试样会存在不同程度的变形. The microstructural evolution during partial remelting of dendritic AlSi Mg alloys was studied with the help of an electrical furnace. The results show that it is diffi- cult to change all the primary α dendrites into the spheroidal α phases, when the dendritic samples of AlSi_7 Mg alloy are remelted under 589 or (597±1)℃ and held on this condition for 5 to 120 min. The results also show that the samples remelted can be deformed under the heavy force, if the holding time is longer under higher temperature.
出处 《北京科技大学学报》 EI CAS CSCD 北大核心 1998年第3期258-261,共4页 Journal of University of Science and Technology Beijing
基金 国家"863"基金资助项目
关键词 重熔 铝合金 铸造 凝固 加热 组织 AlSi_7Mg remelting dendrit
  • 相关文献

参考文献1

共引文献46

同被引文献11

  • 1谢国宏.搅拌铸造法制造颗粒增强铝基复合材料的研究与发展[J].材料工程,1994,22(12):5-7. 被引量:18
  • 2张桓.复合材料轴承[M].北京:科学出版社,1996.43-45.
  • 3陆苏荪.有色铸造合金及其熔炼[M].北京:国防工业出版社,1983.113-117.
  • 4王成守.轴承[M].北京:机械工业出版社,1986.36-38.
  • 5江生.铜及铜合金的焊接[M].北京:化学工业出版社,1979.79-81.
  • 6李时先.石墨材料[M].北京:化学工业出版社,1991.63-65.
  • 7蔡家园.铜及铜合金相图[M].北京:机械工业出版社,1983.28-29.
  • 8骆中安.钢背Al-Pb合金轴瓦轧制成形的研究[M].沈阳:东北大学,1993.25-27.
  • 9Merton C. Flemings. Behavior of metal alloys in the semisolid state[J] 1991,Metallurgical Transactions A(5):957~981
  • 10孙大仁,杨晓红,曹占义,陆有,刘勇兵.铸造铝铅滑动轴承合金的制备及其显微组织[J].特种铸造及有色合金,1998,18(5):24-26. 被引量:25

引证文献4

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部