还原纳米石墨/聚氨酯导电胶的制备与性能研究 被引量:10

Study on preparation and performance of reduced nano-graphite/polyurethane conductive adhesive
下载PDF
导出
摘要 利用异氰酸酯与多元醇在不同的反应条件下制取三种性能不同的聚氨酯(PU)预聚体(PUⅠ、PUⅡ和PUⅢ),然后分别与还原纳米石墨(RNG)、三羟甲基丙烷(TMP)混合制备三种RNG/PU导电胶(RNG/PUⅠ、RNG/PUⅡ和RNG/PUⅢ)。运用多种检测手段对导电胶的导电性能、力学性能和热稳定性能进行了分析。结果表明:随着RNG质量分数的增加,三种导电胶的导电性能均增强,其导电逾渗阀值分别为10.0%、16.7%和20.0%;导电胶的拉伸剪切强度随RNG质量分数的增加呈先升后降的趋势,当w(RNG)=20%时导电胶的拉伸剪切强度为1.37~4.40MPa;RNG的加入使导电胶的热稳定性能明显提高。 Three types reduced nano-graphite(RNG)/polyurethane(PU) conductive adhesive (namely RNG/PUⅠ, RNG/PUⅡ and RNG/PUⅢ) were made by mixed method between RNG and trihydroxylmethylpropane(TMP) and certain PU prepolymers(namely PUⅠ ,PUⅡ or PUⅢ) which were made by reaction between isocyanate and polyalcohol under different reaction conditions. The conductive adhesive performances such as conductive performance, mechanics performance and thermal stability were analysed by manifold testing meanses. The results showed that the electrical conductivities of all conductive adhesives were increased with increase of mass fraction of RNG, and their percolation threshold values were 10.0%, 16.7% and 20.0% respectively. The tensile shear strength of all conductive adhesives had trend of increase-fall with increase of mass fraction of RNG,and tensile shear strengths of conductive adhesives were 1.37-4.40 MPa when mass fraction of RNG was 20%. The thermal stability of conductive adhesives was obviously improved when RNG was introduced in systems.
出处 《中国胶粘剂》 CAS 北大核心 2009年第6期46-51,共6页 China Adhesives
关键词 还原纳米石墨 聚氨酯 预聚体 导电胶 reduced nano-graphite (RNG) polyurethane prepolymer conductive adhesives
  • 相关文献

参考文献12

  • 1OTIENO G,KIM JU-YOUNG. Conductive graphite/ polyurethane composite films using amphiphilic reactive dispersant:Synthesis and characterization[J]. Journal of Industrial and Engineering Chemistry, 2008,14 (2) : 187- 193.
  • 2NOVAK I, KRUPA I, CHODAK I. Electroconductive adhesives based on epoxy and polyurethane resins filled with silver-coated inorganic fillers[J]. Synthetic Metals, 2004, 144(1 ) : 13-19.
  • 3CHEN JING,ZHOU YU-MING,NAN QIU-LI,et al. Synthesis,characterization and infrared emissivity study of polyurethane/TiO2 nanocomposites[J]. Applied Surface Science,2007,253(23) :9 154-9 158.
  • 4SAHA M C,KABIR M E,JEELANI S. Enhancement in thermal and mechanical properties of polyurethane foam infused with nanoparticles[J]. Materials Science and Engineering : A, 2008,479 ( 1-2 ) : 213-222.
  • 5詹中贤.多元醇对聚氨酯胶粘剂性能的影响[J].聚氨酯工业,2006,21(1):28-30. 被引量:13
  • 6NOVAK l, KRUPA I, CHODAK I. Investigation of the correlation between electrical conductivity and elongation at break in polyurethane-based adhesives[J]. Synthetic Metals, 2002,131 ( 1-3 ) : 93-98.
  • 7李大军,严长浩,鲁萍,周岚,吴德峰,张明.膨胀石墨/聚酯导电复合材料的制备与导电行为[J].复合材料学报,2008,25(1):35-39. 被引量:18
  • 8黄仁和,王力.纳米石墨薄片及聚合物/石墨纳米复合材料制备与功能特征研究[J].功能材料,2005,36(1):6-10. 被引量:19
  • 9林韡,于朝生.石墨/环氧树脂导电胶的研究[J].中国胶粘剂,2008,17(6):4-9. 被引量:7
  • 10STANKOVICH S, DIKIN D A, PINER R D, et al. Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide[J]. Carbon, 2007,45 (7) : 1 558- 1 565.

二级参考文献54

共引文献82

同被引文献192

引证文献10

二级引证文献61

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部