摘要
采用金相显微分析法,研究添加Si、Mn及富Ce稀土对工业纯铝中初晶α-Al晶粒度和富Fe相(Al3Fe)形貌的影响。结果表明,Si、Mn和RE对工业纯铝显微组织的影响和作用机制不同。添加Si起到细化初晶晶粒和增加富Fe相含量的作用;添加Mn几乎没有细化初晶,但是降低合金中富Fe相的含量;添加RE不但细化晶粒,还显著降低富Fe相的含量。就各元素的作用机制进行了探讨。
The effects of sihcon, manganese and Ce-riched mixed rare earth on the granularity of primary α-Al and the morphology of Fe-riched phase in industrial pure aluminum were studied by using the metallographic micro-analytical method. Experimental results show that, adding Si, Mn and RE has different effects and different action mechanism on the microstrueture of alloys. The addition of Si can refine the primary α-Al grain and increase the content of Al3Fe phase; the addition of Mn has less effect on refining the grain but reduces the content of Al3 Fe phase; the addition of RE either refines the α-Al grain or greatly reduces the content of Al3 Fe phase. Moreover, the action mechanism of the elements was discussed.
出处
《轻合金加工技术》
CAS
北大核心
2009年第7期48-51,59,共5页
Light Alloy Fabrication Technology
基金
内蒙古自然科学基金重大项目(编号20080103)
关键词
工业纯铝
显微组织
富Fe相
变质
稀土
industrial pure aluminum
microstrueture
Fe-riehed phase
modification
rare earths