摘要
Copper-doped ZnO nanoparticles were synthesized by the sol-gel method.The X-ray diffraction（XRD） result shows that Zn1-xCuxO（x≤0.04） samples are single phase with ZnO-like wurtzite structure,while the secondary phase Cu is observed in a Zn0.95Cu0.05O sample.Magnetic measurements indicate that Zn1-xCuxO（x≤0.04） samples are ferromagnetic at room temperature.A strong green peak（520 nm） was observed except for UV band peak in photoluminescent（PL） spectrum of Zn0.98Cu0.02O.
Copper-doped ZnO nanoparticles were synthesized by the sol-gel method.The X-ray diffraction（XRD） result shows that Zn1-xCuxO（x≤0.04） samples are single phase with ZnO-like wurtzite structure,while the secondary phase Cu is observed in a Zn0.95Cu0.05O sample.Magnetic measurements indicate that Zn1-xCuxO（x≤0.04） samples are ferromagnetic at room temperature.A strong green peak（520 nm） was observed except for UV band peak in photoluminescent（PL） spectrum of Zn0.98Cu0.02O.
基金
Supported by the National Natural Science Foundation of China(No.60778040)
the Science and Technology Program of "11th Five-Year" of Education for Jilin Province,China(Nos.20070161,20070162)