研究了２０９１铝锂合金超塑变形的断裂行为。扫描电镜观察表明，２０９１铝锂合金超塑变形中存在晶内断裂，光学金相观察表明断裂试样存在较活跃的动态再结晶和较多的大轴径比晶粒，透射电镜观察发现断裂试样内部存在较多的晶内位错。研究表明，由于再结晶缩小了大轴径比晶粒的横截面使其在超塑变形的晶粒转动中受到很大的弯曲应力而造成了晶内断裂。
The fracture behaviors in superplastic deformation of 2091 Al Li alloy have been investigated. SEM observations indicated that interior fracture existed in superplastic deformation of 2091 Al Li alloy. Optical metallography observations also indicated that there were active dynamic recrystallization and a lot of grains with great ratio of longitudinal size with latitudinal size in fracture specimen. TEM observations found that lots of interior dislocations were created in fracture specimen. It is indicated that interior fracture in superplastic deformation of 2091 Al Li alloy is caused by great bending stress created by grain rotation due to cross section size of grains with great ratio of longitudinal size with latitudinal size decreased by recrystallization.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
1998年第3期467-471,共5页
The Chinese Journal of Nonferrous Metals
基金
石油天然气总公司中青年创新基金
航空工业总公司航空科学基金