摘要
通过改变焊接区外加气体介质和焊丝熔敷金属中氧、氮、氢含量的分析,对自保护药芯焊丝焊缝气孔的形成原因及影响因素进行了研究.研究结果表明:氧和氮是影响自保护药芯焊丝焊缝气孔产生的主要原因,氧对自保护药芯焊丝焊缝气孔的产生具有加剧作用,一般情况下,氢不是自保护药芯焊丝焊缝气孔产生的主要因素.
The causes and the influence factors of porosity in the weld of self-shieldedflux-cored wire (SSFCW) were studied through providing different gaseous stream flowinto arc area and determining the content of oxygen, nitrogen and hydrogen in depositmetal. As it turned out: that oxygen and nitrogen content are main influence factors forformation of porosity in the weld of SSFCW, oxygen can rapidly increase the quantityof porosity in the weld of SSFCW and hydrogen content is not of the main influencefactors of the porosity formation in the weld of SSFCW.
出处
《北京工业大学学报》
CAS
CSCD
1998年第3期89-92,共4页
Journal of Beijing University of Technology
基金
北京市高教局资助
关键词
药芯焊丝
自保护
气孔
氧
氮
氢
焊缝
flux-cored wire, self-shield, pore sensitivity