摘要
The solution heat treatment,cold deformation and subsequent aging were performed on CuMoCr alloy.And the influence of deformation and aging treatment on the electrical conductivity of CuMoCr alloy was studied through metallograph,transmission electron microscopy(TEM) and electrical conductivity measurement.Results show that deformation without subsequent aging can reduce the electrical conductivity of CuMoCr alloy,but deformation followed by the optimum aging treatment can effectively improve the electrical conductivity of CuMoCr alloy.Aging at 500 ℃ for 4 h after 80% deformation,the much better electrical conductivity of CuMoCr alloy can be obtained.Reduction of Cr content in the Cu matrix could be the reason for the enhancement of electrical conductivity.
The solution heat treatment,cold deformation and subsequent aging were performed on CuMoCr alloy.And the influence of deformation and aging treatment on the electrical conductivity of CuMoCr alloy was studied through metallograph,transmission electron microscopy（TEM） and electrical conductivity measurement.Results show that deformation without subsequent aging can reduce the electrical conductivity of CuMoCr alloy,but deformation followed by the optimum aging treatment can effectively improve the electrical conductivity of CuMoCr alloy.Aging at 500 ℃ for 4 h after 80% deformation,the much better electrical conductivity of CuMoCr alloy can be obtained.Reduction of Cr content in the Cu matrix could be the reason for the enhancement of electrical conductivity.