摘要
研究了Al对LiBH4吸放氢性能的影响。结果表明,Al的添加可使LiBH4起始放氢温度降低至300℃左右,且主要放氢过程的温度范围随着Al含量的增加而逐渐降低;可逆性研究表明,放氢后的LiBH4/Al混合体系在600℃、10MPa条件下实现可逆吸氢,这明显低于单一LiBH4的可逆吸氢条件。LiBH4/Al吸放氢性能改善的原因是由于化合物LiAl和AlB2的生成。
The effect of AI addition on the hydrogen storage performance of LiBH4 was investigated. It is indicated that the onset dehydrogenation temperature of LiBH4/Al mixture is decreased to about 300℃. The main hydrogen release shifts to low temperature with the increase of Al content. Furthermore, the dehydrogenated LiBH4/Al sample can be rehydrogenated at 600 ℃ and 10 MPa, significantly lower than that of the plan LiBH4. The improvement of hydrogen storage properties in LiBH4/Al system is due to the formation of LiAl and AlB2 compounds during the dehydrogenation.