以桐油酸酐(TOA)和三(2-羟乙基)异氰脲酸酯(THEIC)为原料,合成了赛克-桐油酸酐(TTOA)固化剂,然后用TTOA固化环氧树脂E44得到TTOA-E44树脂。TTOA-E44树脂的热差分析(TGA)的实验结果表明:固化树脂的耐热指数高达174℃,表观分解温度高达356℃,抗热老化性能和弯曲强度优于同类固化剂的固化物。
A curing agent of TTOA with excellent thermal property was synthesized from eleostearic acid anhydride and tri （2 - hydroxyethyl） isocyanurate, which was used to cure the E44 epoxy resin forming T-FOA -E4d resin. The findings of TGA analysis showed that the heat -resistant index of TFOA -E44 resin has up to 174 ℃ and the apparent decomposition temperature over 356 ℃. Its thermal ageing property and bending strength was better than other similar products.