通过固相反应法制备了YBa2Cu3Ox/Ag和Bi2Sr2CaCu2Ox/Ag固体自润滑材料。采用XRD和SEM检测了材料的成分以及相结构。XRD结果表明,所制备的YBa2Cu3Ox/Ag和Bi2Sr2CaCu2Ox/Ag固体自润滑复合材料都是由超导相和Ag相组成。采用销-盘式摩擦试验机研究了试样在常温下的摩擦学性能。结果表明,室温下纯YBa2Cu3Ox的摩擦系数为0.68～0.95,当掺杂15%(质量分数)Ag时,摩擦系数减小到最低,为0.11左右;纯Bi2Sr2CaCu2Ox的摩擦系数为0.21～0.22,当掺杂10%(质量分数)Ag时,摩擦系数降低到最低,为0.18左右。在超导体中添加Ag可有效改善材料的摩擦学性能。Ag可在材料摩擦接触表面形成一层Ag膜,从而有效改善接触表面,达到减小摩擦力的效果。
The YBa2Cu3Ox/Ag and Bi2Sr2CaCu2Ox/Ag self-lubricating composites are prepared using powder metallurgic method. The structure and morphology of the as-synthesized samples are characterized by XRD and SEM. XRD analysis indicate that YBa2Cu3Ox/Ag and Bi2Sr2CaCu2Ox/Ag self-lubricating composites are composed of super-conductor phase and Ag phase. The tribological properties of the composites are studied by pin-on-disk tribometer at room temperature. The results show that the lowest friction coefficient of YBa2Cu3Ox/Ag composites is 0.11, littler than that of Bi2Sr2CaCu2Ox/Ag composites （0.18）. The tribological properties of the superconductor can be improved due to the doping of Ag, because the Ag films generated at the contract zone of the composites, improve the tribological properties of the composites.
出处
《材料导报》
EI
CAS
CSCD
北大核心
2009年第20期55-57,共3页
Materials Reports
基金
国家自然科学基金(50372026)