Sodium chloride(NaCl)was added as a space holder in synthesis of porous titanium by using metal injection molding(MIM)method.The microstructure and mechanical properties of porous titanium were analyzed by mercury porosimeter, scanning electron microscope(SEM)and compression tester.The results show that the content of NaCl influences the porosity of porous titanium significantly.Porous titanium powders with porosity in the range of 42.4%-71.6%and pore size up to 300μm were fabricated.The mechanical test shows that with increasing NaCl content,the compressive strength decreases from 316.6 to 17.5 MPa and the elastic modulus decreases from 3.03 to 0.28 GPa.
Sodium chloride (NaCl) was added as a space holder in synthesis of porous titanium by using metal injection molding(MIM) method. The microstructure and mechanical properties of porous titanium were analyzed by mercury porosimeter, scanning electron microscope(SEM) and compression tester. The results show that the content of NaC1 influences the porosity of porous titanium significantly. Porous titanium powders with porosity in the range of 42.4% 71.6% and pore size up to 300 μm were fabricated. The mechanical test shows that with increasing NaCI content, the compressive strength decreases from 316.6 to 17.5 MPa and the elastic modulus decreases from 3.03 to 0.28 GPa.
出处
《中国有色金属学会会刊:英文版》
EI
CSCD
2009年第5期1174-1179,共6页
Transactions of Nonferrous Metals Society of China
基金
Project(30770576)supported by the National Natural Science Foundation of China
Project(2007AA03Z114)supported by Hi-tech Research and Development Program of China