摘要
采用磷渣为原料,通过合理的配料方案,成功制备了性能优异的水泥熟料。通过岩相观察和XRD分析结果表明,实验所用生料易烧性较好,并随温度提高而明显改善,所制备的水泥熟料的主晶相是C3S和C2S。
Through proper designed plan,high quality cement clinker was obtained by using phosphorus slag as raw material.Samples were investigated by petrography analysis（PA） and X-ray diffraction（XRD）,the results show that sinterability of cement raw materials was fine and was clearly improved by increasing the temperature;the main phases of the sintered cement clinker were C3S and C2S.
出处
《建材世界》
2009年第4期40-42,共3页
The World of Building Materials
关键词
水泥熟料
磷渣
易烧性
安定性
cement clinker
phosphorus slag
sinterability
stability