摘要
以高纯、超细的镁铝尖晶石粉末作为起始原料,采用真空热压烧结与热等静压法相结合制备透明尖晶石陶瓷材料(TMAC)。测试了TMAC材料的高温性能,并探讨其可能的应用。从室温到250℃,材料的抗弯强度没有发生明显的变化;从室温到900℃的热膨胀系数和电阻率测试结果表明该材料有良好的稳定性和电绝缘性能;经过从室温到1100℃的退火,TMAC的红外透过率和面形均未发生明显变化,表明材料有比较好的耐高温性能。
In this paper, transparent ceramic spinel was fabricated by hot pressing in vacuum combined with hot isostatic pressing （HIP）. Highly pure ultra fine spinel powder was used as a starting material. Some high temperature performances were also measured. From room temperature to 250 ℃, the flexural strength did not have large change. And the results of the coefficient of thermal expansion and the conductivity from room temperature to 900 ℃ shows that TMAC has good stability and electrical insulation properties. After fired under the temperature of 1100℃, there isn＇t obvious change of the transmittance and mophores of the spinel, this indicates that the transparent spinel is a good IR window material which can resist the high temperature.
出处
《硅酸盐通报》
CAS
CSCD
北大核心
2009年第B08期190-193,共4页
Bulletin of the Chinese Ceramic Society
关键词
透明陶瓷
尖晶石
高温性能
应用
transparent ceramic
spinel
high temperature performance
application