连铸坯表面振痕形成机理研究 被引量：1

Study on Formation Mechanism of Oscillation Mark on CC Strand Surface
原文传递
导出
摘要 介绍了几种连铸坯表面振痕形成的机理,并对各种机理的优缺点进行了阐述。 The mechanism of CC slab oscillation marks was introduced, the excellences and the defects of these mechanisms were expatiated.
作者 王贺利 雷作胜
机构地区 太原钢铁集团有限公司 上海大学
出处 《连铸》 2009年第5期13-17,共5页 Continuous Casting
关键词 方坯 表面缺陷 振痕 形成机理 结晶器 slab surface defect oscillation mark formation mechanism mold
分类号 TF777.2 [冶金工程—钢铁冶金]
  • 相关文献

参考文献10

  • 1Savage J. A New Reciprocation Mould Cycle to Improve Surface Quality of Continuous Casting Steel[J]. Iron and Coal Trade Review, 1961,182(4): 787.
  • 2Samarasekera I V,Brimacombe J K. Thermal and Mechanical Behaviour of Continuous Casting Billet Mould[J]. Ironmaking and Steelmaking, 1982, (1) : 1.
  • 3Samarasekera I V, Anderson D L, Brimacombe J K. The Thermal Distortion of Continuous Casting Billets Mould[J]. Metallurgical Transactions B,1982, 13B(3) : 91.
  • 4Szekely J,Evans J W,Brimacombe JK.金属初级加工过程的数学和物理模拟[M].蔡开科译.北京:冶金工业出版社,1992.
  • 5Szekeres E S. Overview of Mould Oscillation in Continuous Casting[J]. Iron and Steel Engineer, 1996, (7):29.
  • 6Takeuchi E, Brimacombe J K. The Formation of Oscillation Marks in the Continuous Casting of Steel Slabs[J]. Metallurgical Transactions B, 1984, 15B(9): 493.
  • 7TAKEUCHI Shuji, MIKI Yuji, ITOYAMA Seiji, et al. Control of Oscillation Mark Formation During Continuous Casting[J]. Steelmaking, 1991.
  • 8Lainea E, Busturial J C. The E. L. V. Solidification Model in Continuous Casting Billets Moulds Using Casting Powder [C]. Proceedings of Ist European Conference on Continuous Casting. Florence, Italy, 1991,1621.
  • 9Fredriksson H,Elfsberg J. Thoughts About the Initial Solidi- fication Process During Continuous Casting of Steel[J]. Scandinavian Journal of Metallurgy, 2002, 31(10): 292.
  • 10雷作胜,任忠鸣,张邦文,邓 康.连铸结晶器振动下弯月面处温度波动的模拟实验[J].金属学报,2002,38(8):877-880. 被引量：8

二级参考文献4

共引文献7

同被引文献10

引证文献1

二级引证文献4

连铸
2009年 第5期

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部