摘要
研究掺杂BaTiO3来提高铬酸镧材料的电阻。通过对烧结时间、掺杂BaTiO3比例的研究,发现掺杂Ba-TiO3铬酸镧材料的电阻率随烧结时间的增大呈现下降趋势。掺杂质量比1%~2%的铬酸镧在烧结20h后,电阻率基本稳定,使铬酸镧材料电阻可调。
Improvement on LaCrO3 resistivity by doping BaTiO3 was studied in this paper.It was found that the resistivity of LaCrO3 after doping BaTiO3 decreases with sintering time,and tends to be a constant value after sintering for 20 hours.The LaCrO3 doped by 1%～2% BaTiO3makes itself to be useful resistor.