The volume fraction and morphology of the TCP-phase formed in two kinds of Ni- Mo-Cr-Re superalloys under different heat treatment conditions were investigated in this paper. In Re-5% alloy, with increasing of the heat treatment temperature and prolonging the holding time, the volume fraction of TCP-phase decreased and the TCP-phase size increased. At relatively lower temperature, the TCP-phase prefers to present in the dendrite cores. In Re-10% alloy, the volume fraction and size have the same change tendency as that of in Re-5% alloy, but the morphology will change from needle-like and block-like to sphere when the temperature increases. The TCP-phases formed in these two Ni-Mo-Cr-Re alloys are σ and P phase.
The volume fraction and morphology of the TCP-phase formed in two kinds of Ni- Mo-Cr-Re superalloys under different heat treatment conditions were investigated in this paper. In Re-5% alloy, with increasing of the heat treatment temperature and prolonging the holding time, the volume fraction of TCP-phase decreased and the TCP-phase size increased. At relatively lower temperature, the TCP-phase prefers to present in the dendrite cores. In Re-10% alloy, the volume fraction and size have the same change tendency as that of in Re-5% alloy, but the morphology will change from needle-like and block-like to sphere when the temperature increases. The TCP-phases formed in these two Ni-Mo-Cr-Re alloys are σ and P phase.
基金
the financial support from the National High Magnetic Field Laboratory under NSF DMR-0084173