摘要
本文首先利用正交试验确定了液相沉淀法合成纳米AgO粉体的最佳制备条件。接着研究了最佳条件下制备的纳米AgO粉体的性能。UV-vis DRS分析结果表明,反射率随着AgO含量的增加而降低,高纯度AgO在400nm-1100nm波长范围内具有较强的吸收能力。TG-DTG分析结果表明,在N2气氛下,AgO热分解为Ag2O的温度范围为100℃-200℃,Ag2O热分解为Ag的温度范围为400℃-450℃。
In this paper, the nano-sized silver (I, III) oxide was prepared by chemical deposition method with orthogonal Experiments. Then the prepared samples were characterized. In the UV-vis DRS spectrum,the reflectivity decreased with the increment of AgO purity, and it showed that high content of AgO was with high absorption rate in the 400-1100nm wavelength range. According to the result of TG-DTG test,the transformation temperature range of AgO to Ag20 was from 100℃ to 200℃, and that of Ag20 to Ag was from 400℃ to 450℃ in nitrogen atmosphere.