Friction stir welding of 5052 aluminum alloy plates 被引量:8

Friction stir welding of 5052 aluminum alloy plates
下载PDF
导出
摘要 Friction stir welding between 5052 aluminum alloy plates with a thickness of 2 mm was performed. The tool for welding was rotated at speeds ranging from 500 to 3000 r/min under a constant traverse speed of 100 mm/min. The results show that at all tool rotation speeds, defect-free welds are successfully obtained. Especially at 1000, 2000 and 3000 r/min, the welds exhibit very smooth surface morphologies. At 500, 1000, and 2000 r/min, onion ring structure is clearly observed in the friction-stir-welded zone (SZ). In addition, the onion ring structure region becomes wider as the tool rotation speed is increased. The gain size in the SZ is smaller than that in the base metal, and is decreased with a decrease of the tool rotation speed. In all tool rotation speeds, the SZ exhibits higher average hardness than the base metal. Especially at 500 r/min, the average hardness of the SZ reaches a level about 33% greater than that of the base metal. At 500, 1 000 and 2 000 r/min, the tensile strength of the friction stir welded (FSWed) plates is similar to that of the base metal (about 204 MPa). The elongation of the FSWed plates is lower than that of the base metal (about 22%). However, it is noticeable that the maximum elongation of about 21% is obtained at 1 000 r/min. Friction stir welding between 5052 aluminum alloy plates with a thickness of 2 mm was performed. The tool for welding was rotated at speeds ranging from 500 to 3 000 r/min under a constant traverse speed of 100 mm/min, The results show that at all tool rotation speeds, defect-free welds are successfully obtained. Especially at 1 000, 2 000 and 3 000 r/min, the welds exhibit very smooth surface morphologies, At 500, I 000, and 2 000 r/min, onion ring structure is clearly observed in the friction-stir-welded zone (SZ). In addition, the onion ring structure region becomes wider as the tool rotation speed is increased. The gain size in the SZ is smaller than that in the base metal, and is decreased with a decrease of the tool rotation speed. In all tool rotation speeds, the SZ exhibits higher average hardness than the base metal. Especially at 500 r/min, the average hardness of the SZ reaches a level about 33% greater than that of the base metal. At 500, 1 000 and 2 000 r/min, the tensile strength of the friction stir welded (FSWed) plates is similar to that of the base metal (about 204 MPa). The elongation of the FSWed plates is lower than that of the base metal (about 22%). However, it is noticeable that the maximum elongation of about 21% is obtained at 1 000 r/min.
出处 《中国有色金属学会会刊:英文版》 CSCD 2009年第B09期23-27,共5页 Transactions of Nonferrous Metals Society of China
关键词 搅拌摩擦焊接 铝合金板 旋转速度 焊接工具 表面形貌 环形结构 抗拉强度 伸长率 friction stir welding aluminum alloy microstructure mechanical properties
  • 相关文献

参考文献10

  • 1THOMAS W M, NICHOLAS E D. Friction stir welding for the transportation industries[J]. Mater Design, 1997, 18(4/6): 269-273.
  • 2SHIGEMATSU I, KWON Y J, SUZUKI K, IMAI T, SAITO N. Joining of 5083 and 6061 aluminum alloys by friction stir welding[J]. J Mater Sci Lett, 2003, 22(5): 353-356.
  • 3SHIGEMATSU I, SUZUKI K, IMAI T, KWON Y J, SAITO N. Friction stir welding of recycled A6061 aluminum plates fabricated by hot-extrusion of machined chips[J]. J Mater Sci, 2005, 40(11): 2971-2974.
  • 4KANNAN M B, DIETZEL W, ZENG R, ZETTLER R, SANTOS J F D. A study on the SCC susceptibility of friction stir welded AZ31 Mg sheet[J]. Mater Sci Eng A, 2007, 460/461: 243-250.
  • 5DARRAS B M, KHRAISHEH M K, ABU-FARHA F K, OMAR M A. Friction stir processing of commercial AZ31 magnesium alloy[J]. J Mater Proc Tech, 2007, 191(1/3): 77-81.
  • 6THOMAS W M, NICHOLAS D E, NEEDHAM J C, MURCH M G, TEMPLESMITH P, DAWES C J. Friction stir butt welding. GB Patent Application. US Patent, 5460317[P]. 1995.
  • 7KIM H Y, SOHN W H, HONG S H. High temperature deformation of Ti-(46-48)Al-2W intermetallic compounds[J]. Mater Sci Eng A, 1998, 251(1/2): 216-225.
  • 8FURU T, SHERCLIFF H R, BAXTER G J, SELLARS C M. The influence of transient deformation conditions on recrystallization during thermomechanical processing of an Al-1%Mg alloy[J]. Acta Mater, 1999, 47(8): 2377-2389.
  • 9KIM S I, YOO Y C. Dynamic recrystallization behavior of AISI 304 stainless steel[J]. Mater Sci Eng A, 2001, 311 (1/2): 108-113.
  • 10KWON Y J, SHIGEMATSU I, SAITO N. Production of ultra-fine grained aluminum alloy using friction stir process[J]. Mater Trans, 2003, 44(7): 1343-1350.

同被引文献70

  • 1王刚,曲文卿,赵海云,宋民远,董春林,李光,栾国红.搅拌摩擦焊材料塑性流动研究现状[J].航空制造技术,2011,0(8):52-56. 被引量:3
  • 2王孟君,黄电源,姜海涛.汽车用铝合金的研究进展[J].金属热处理,2006,31(9):34-38. 被引量:97
  • 3林刚,林惠国.铝合金应用手册[M].北京:机械工业出版社,2006.
  • 4Scialpi A, De Filippis L A C, Cavaliere P.Influence of shou- lder geometry on microstructure and mechanical properties of friction stir welded 6082 aluminium alloy[J].Materials and Design ,2007,28(4): 1124-1129.
  • 5Skillingberg M,Green J.Almninum applications in the rail industry[J].Light Metal Age ,2007,65(5): 8-13.
  • 6周万盛,姚君山.锅及铝合金的焊接[M].北京:机械工业出版社,2006.
  • 7Mishra R S, Ma Z Y.Friction stir welding and processin[J]. Materials Science and Engineering R, 2005,50(1-2): 1-78.
  • 8Hatamleh O, Hill M, Forth S,et al.Fatigue crack growth per- formance of peened friction stir welded 2195 aluminum alloy joints at elevated and cryogenic temperatures [J].Mat- erials Science and Engineering A, 2009,519(1-2) : 61-69.
  • 9Liu H J,Chen Y C,Feng J C.Friction stir welding chara- cteristics of 6061-T6 aluminum alloy sheet[J].Transactions of Nonferrous Metals Society of China,2005,15(2):43-46.
  • 10Jata K V ,Semiatin S LContinuous dynamic recrystallization during friction stir welding of high strength aluminum alloys [J].Scripta Materialia, 2000,43(8) : 743-749.

引证文献8

二级引证文献32

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部