用X射线衍射ODF分析方法解析了在电场时效过程中2014铝合金织构的形成和演变机理.结果表明:在电场时效过程中2014铝合金的主织构始终是{001}〈210〉织构,而非电场时效其主织构随着时效时间的延长由{001}〈210〉织构(6 h和8 h)转变为{001}〈100〉立方织构(10 h),然后由{001}〈100〉立方织构转变为{011}〈100〉织构(12 h).这主要是电场时效降低了固溶处理2014铝合金样品的储存能,从而抑制其回复所致.
The mechanism of texture formation and evolution for 2014 aluminium alloy during an electric field aging was investigated by X-Ray ODF analysis. The results show that the main texture components of the samples aged under the electric field is unchangeably the {001}(210) component. In constrast, the main texture of the samples aged without an electric field change from {001}(210)(6 h and 8 h) to {001}(100) cube component (10 h) and then to {011}(100)(12 In) with the increase of the aging time. This is mainly due to the decrease of stored energy of the solid solution by the applied electric field, which accordingly restrains the recovery of the 2014 aluminum alloy.
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2009年第5期490-494,共5页
Chinese Journal of Materials Research
基金
国家自然科学基金委员会与上海宝山钢铁集团公司联合基金50374028
博士点基金20050145030资助项目~~
关键词
金属材料
电场时效
织构
2014铝合金
ODF
metallic materials, electric field aging, texture, 2014 aluminum alloy, ODF