摘要
采用光学显微镜、扫描电镜及X射线衍射等对Mg-RE(Nd,Y)-0.48Zn-0.52Zr合金组织及相组成进行了分析。对2种合金的挤压态试样进行了室温力学性能及高温力学性能试验,并与T5热处理后进行比较。Mg-Nd-0.48Zn-0.52Zr合金在300℃时的抗拉强度为79.00MPa,Mg-Nd-Y-0.48Zn-0.52Zr合金在330℃时的抗拉强度为202.53MPa,试验结果表明,添加Y对提高合金高温抗拉强度有明显的作用。
Microstructure and phase constituent of Mg-RE(Nd, Y)-0.48Zn-0.52Zr alloy were analyzed by OM (optical microscope), SEM (scanning electron microscope) and XRD (X-ray diffraction). Meanwhile, the mechanical properties at room temperature and at high temperature of two kinds of as-extruded samples were tested, and they were compared with those of extrusion +T5 heat treated ones. The results show that tensile strength of Mg-RE(Nd)-0.48Zn-0.52Zr reaches 79MPa at 300℃ while tensile strength of Mg-RE(Y)-0.48Zn-0.52Zr reaches 202.53MPa at 330℃. The Y element plays the obvious role in improving elevated tensile strength of the alloy.