Three kinds of superalloys were prepared by spray deposited process. The analysis results of microstructures and mechanical properties indicate that the spray deposited preforms with higher integral densification and the oxygen content in each kind of superalloy was very low. The microstructures are consisted of fine grain without dendritic equi-axed. The spray deposited superalloys possessed good ductility. The forging experiment displays that even though the once deformation of spray deposited GH742 alloy more than 60%, the crack can not be found. Meanwhile, the mechanical properties of spray deposited superalloys are significantly increased.
Three kinds of superalloys were prepared by spray deposited process. The analysis results of microstructures and mechanical properties indicate that the spray deposited preforms with higher integral densification and the oxygen content in each kind of superalloy was very low. The microstructures are consisted of fine grain without dendritic equi-axed. The spray deposited superalloys possessed good ductility. The forging experiment displays that even though the once deformation of spray deposited GH742 alloy more than 60%, the crack can not be found. Meanwhile, the mechanical properties of spray deposited superalloys are significantly increased.
基金
Funded by the Innovation Fund for Outstanding Scholar of Henan Province(No. 0621000700)