Superplasticity and Fracture Behavior of Fine Grained 5083 Al Alloy

Superplasticity and Fracture Behavior of Fine Grained 5083 Al Alloy
下载PDF
导出
摘要 The microstructure with uniform equiaxed fine gain was obtained by the thermo-mechanical processing (TMP) for the 5083 Al alloy (Al-4.56%Mg-0.61%Mn) plate. Uniaxial tensile test was carried out at a temperature range of 500-570 ℃ and a strain rate range of 4.17×10^-4 s-1^- 1×10^- 2 s^- 1. Maximum tensile elongation 530% was obtained at 550 ℃ and strain rate ε& =4 .17×10^-4 s^-1. Dislocations were observed in grain interiors and at grain boundaries during uniaxial tensile deformation by transmission electronic microscopy (TEM), respectively. Results show that the grain boundary sliding (GBS) accommodated by dislocation motion is the principal reason for superplastic deformation. The cavities and fracture were observed during uniaxial tensile deformation of the alloy by scanning electronic microscopy (SEM), indicating that linkage of cavities in large region would induce failure of the material. Moreover, presence of liquid phase at grain boundary also affects the superplastic deformation and behavior of cavities. The microstructure with uniform equiaxed fine gain was obtained by the thermo-mechanical processing (TMP) for the 5083 Al alloy (Al-4.56%Mg-0.61%Mn) plate. Uniaxial tensile test was carried out at a temperature range of 500-570 ℃ and a strain rate range of 4.17×10^-4 s-1^- 1×10^- 2 s^- 1. Maximum tensile elongation 530% was obtained at 550 ℃ and strain rate ε& =4 .17×10^-4 s^-1. Dislocations were observed in grain interiors and at grain boundaries during uniaxial tensile deformation by transmission electronic microscopy (TEM), respectively. Results show that the grain boundary sliding (GBS) accommodated by dislocation motion is the principal reason for superplastic deformation. The cavities and fracture were observed during uniaxial tensile deformation of the alloy by scanning electronic microscopy (SEM), indicating that linkage of cavities in large region would induce failure of the material. Moreover, presence of liquid phase at grain boundary also affects the superplastic deformation and behavior of cavities.
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2009年第5期800-804,共5页 武汉理工大学学报(材料科学英文版)
关键词 5083 Al alloy SUPERPLASTICITY CAVITIES liquid phase 5083 Al alloy superplasticity cavities liquid phase
  • 相关文献

参考文献12

  • 1Zhang Kaifeng Ph D,Yin Deliang Ph D,Wang Guofeng,Han Wenbo.Superplastic deformation behavior of hot-rolled AZ31 magnesium alloy sheet at elevated temperatures[J].Journal of Wuhan University of Technology - Mater Sci Ed.2006(3)
  • 2R. Verma,P. A. Friedman,A. K. Ghosh,S. Kim,C. Kim.Characterization of superplastic deformation behavior of a fine grain 5083 Al alloy sheet[J].Metallurgical and Materials Transactions A.1996(7)
  • 3Li F,,Roberts W T,Bate P S.Superplasticity and the Development of Dislocation Structures in an Al-4.5% Mg Alloy[].Acta Materialia.1996
  • 4Hsiao I C,Huang J C.Development of Low Temperature Superplasticity in Commercial 5083 Al-Mg Alloys[].Scripta Materialia.1998
  • 5Lee S W,Yeh J W.Superplasticity of 5083 Alloys with Zr and Mn Additions Produced by Reciprocating Extrusion[].Journal of Materials Science.2007
  • 6Pan Fusheng,Zhang Dingfei, et al.Aluminum Alloy and Its Application[]..2006
  • 7Wen Jiuba,Yang Yulin,Yang Yongshun, et al.Application and Technique of Superplasticity[]..2005
  • 8Lin Gang,Lin Huiguo,Zhao Yuqing.Applied Handbook of Aluminum Alloy[]..2006
  • 9Higashi K,Nieh T G,Mabuchi M, et al.Effect of Liquid Phases on the Tensile Elongation of Superplastic Aluminum Alloys and Composites[].Scripta Metallurgica.1994
  • 10Kaifeng ZHANG,Deliang YIN,Guofeng WANG,Wenbo HAN.Cavitation Behavior during Superplastic Deformation of AZ31 Magnesium Alloy[J].Journal of Materials Science & Technology,2005,21(4):510-514. 被引量:1

二级参考文献13

  • 1M.A.Michael and H.Baker: ASM Specialty HandbookMagnesium and Magnesium Alloys, ASM International,Ohio, 1999, 75.
  • 2M.T.Perez-Prado and O.A.Ruano: Scripta Mater., 2002,46, 149.
  • 3B.L.Mordike and T.Ebert: Mater. Sci. Eng., 2001, 302A,37.
  • 4Shyong Lee, Yung-Hung Chen and Jian-Yih Wang: J.Mater. Proc. Tech., 2002, 124, 19.
  • 5H.Takuda, T.Enami and K.Kubota: J. Mater. Proc.Tech., 2000, 101, 281.
  • 6H.Takuda, H.Fujimoto and N.Hatta: J. Mater. Proc.Tech., 1998, 80, 513.
  • 7Y.H.Wei, Q.D.Wang and Y.P. Zhu: Mater. Sci. Eng.,2003, A360, 107.
  • 8H.Watanabe, T.Mukai and K.Ishikawa: Scripta Mater.,2002, 46, 851.
  • 9J.C.Tan and M.J.Tan: Scripta Mater., 2002, 47, 101.
  • 10T.G.Nieh, J.Wadsworth and O.D.Sherby: Superplasticity in Metals and Ceramics, Cambridge University Press,Cambridge, 1997, 225.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部