Novel Y-shaped block copolymers of poly（ethylene glycol） and poly（N-isopropylacrylamide）, PEG-b-（PNIPAM）2, were successfully synthesized through atom transfer radical polymerization （ATRP）. A difunctional macroinitiator was prepared by esterification of 2,2-dichloroacetyl chloride with poly（ethylene glycol） monomethyl ether （PEG）. The copolymers were obtained via the ATRP ofN-isopropylacrylamide （NIPAM） at 30℃ with CuCl/Me6TREN as a catalyst system and DMF/H2O （v/v = 3：1） mixture as solvent. The resulting copolymers were characterized by gel permeation chromatography （GPC） and ^1H NMR. These block copolymers show controllable molecular weights and narrow molecular weight distributions （PDI 〈 1.15）. Their phase transition temperatures and the corresponding enthalpy changes in aqueous solution were measured by differential scanning calorimetry （DSC）. As a result, the phase transition temperature of PEG45-b-（PNIPAM55）2 is higher than that of PNIPAM, however, the corresponding enthalpy change is much lower, indicating the significant influence of the macromolecular composition and architecture on the phase transition.
Novel Y-shaped block copolymers of poly（ethylene glycol） and poly（N-isopropylacrylamide）, PEG-b-（PNIPAM）2, were successfully synthesized through atom transfer radical polymerization （ATRP）. A difunctional macroinitiator was prepared by esterification of 2,2-dichloroacetyl chloride with poly（ethylene glycol） monomethyl ether （PEG）. The copolymers were obtained via the ATRP ofN-isopropylacrylamide （NIPAM） at 30℃ with CuCl/Me6TREN as a catalyst system and DMF/H2O （v/v = 3：1） mixture as solvent. The resulting copolymers were characterized by gel permeation chromatography （GPC） and ^1H NMR. These block copolymers show controllable molecular weights and narrow molecular weight distributions （PDI 〈 1.15）. Their phase transition temperatures and the corresponding enthalpy changes in aqueous solution were measured by differential scanning calorimetry （DSC）. As a result, the phase transition temperature of PEG45-b-（PNIPAM55）2 is higher than that of PNIPAM, however, the corresponding enthalpy change is much lower, indicating the significant influence of the macromolecular composition and architecture on the phase transition.
基金
support from the National Natural Science Foundation of China(No. 20134020)
the Visiting Scholar Project of Shandong Province of China(No.20081001)
the Science Research Fund of Shandong Jiaotong University of China(No.Z200802)