摘要
研究了真空高压气淬热处理工艺对2Cr13钢的组织和性能的影响。结果表明:随着气淬压力的升高,2Cr13钢的强度和硬度有所提高,伸长率和冲击韧度有所降低,断面收缩率和淬透性的变化不大;采用真空高压气淬工艺处理试样的组织为均匀细小的板条状淬火马氏体组织,力学性能及淬透性满足标准要求;而且试样表面光洁,呈银亮色,可免除淬火后的清洗;可替代现有的真空油淬工艺。
The effect of vacuum high pressure gas quenching on the microstructure and mechanical properties was studied in 2Cr13 steel. The experimental results showed that with pressure increased, the strength and the hardness increased, the elongation and the toughness were lower lightly, and reduction of area and harden ability were changed little. After high pressure gas quenching , the microstructure of the sample was uniformly fine battenshaped quenched martensite, the mechanical properties and the harden ability met standard requirement. Furthermore, the surface of the sample was much clean, the silvery-bright,may remove the cleansing. Therefore, current vacuum oil quenching process may be replaced.
出处
《理化检验(物理分册)》
CAS
2009年第11期675-677,共3页
Physical Testing and Chemical Analysis(Part A:Physical Testing)
关键词
2Crl3钢
真空高压气淬
真空油淬
显微组织
力学性能
淬透性
2Cr13 steel
vacuum high pressure gas quenching
vacuum oil quenching
microstructure
mechanical properties
harden ability