Mg-Gd-Y-Nd-Zr合金铸锭的均匀化 被引量:7

Homogeneity of Mg-Gd-Y-Nd-Zr alloy as-cast
下载PDF
导出
摘要 采用光学金相、差热分析、扫描电镜、能谱分析和拉伸试验等方法,对比研究Mg-Gd-Y-Nd-Zr合金铸锭非平衡凝固组织熔点(539℃)以下(520℃)和先于520℃保温再在非平衡凝固组织熔点以上(560℃)保温这2种不同均匀化制度对合金组织和力学性能的影响。结果表明:Mg-Gd-Y-Nd-Zr合金采用520℃保温均匀化后,尽管伪共晶基本消除,但残留较多富稀土粒子,进一步采用560℃保温均匀化后,不仅非平衡组织能在较短的时间内消除,而且富稀土粒子相明显减少,伸长率提高50%以上;减少熔炼时形成游离稀土粒子和在高于非平衡凝固组织熔点以上保温均匀化是提高该合金伸长率的有效途径。 The influence of two different homogenization heat treatment,one at temperature below the melting point of pseudo-eutectic(MPPE,539℃)and another include treating below MMPE followed by treating above MPPE,on the microstructures and mechanical properties of Mg-Gd-Y-Nd-Zr alloy was investigated with OM,DTA,SEM,EDS and tensile test.The results show that,almost all the pseudo-eutectics disappear after the homogenization heat-treatment at 520℃,but some rare-earth-rich particles remain.While after the further homogenization heat-treatment at 560℃,the amount of rare-earth particles decreases dramatically.Therefore,the elongation rate of the two-stage homogenized samples increases by 50%with the decrease of the rare-earth-rich particles.This reveals that decreasing the dissociatived rare-earth particles and being homogeneity-heat-treated at temperature more than the MPPE are effective ways to improve the elongation of the present Mg-Gd-Y-Nd alloy.
出处 《中南大学学报(自然科学版)》 EI CAS CSCD 北大核心 2009年第5期1240-1244,共5页 Journal of Central South University:Science and Technology
基金 国家基础研究项目(5133001E)
关键词 镁合金 稀土 热处理 显微组织 力学性能 magnesium alloy rare-earth heat-treatment microstructure mechanical property
  • 相关文献

参考文献15

  • 1Alves H, Koster U, Aghion E, et al. Environmental behavior of magnesium and magn-esium alloys[J]. Materials Technology, 2001, 16(2): 110-126.
  • 2I.M.Baghni,吴荫顺,李久青,杜翠薇,张巍.Mechanical properties and potential applications of magnesium alloys[J].中国有色金属学会会刊:英文版,2003,13(6):1253-1259. 被引量:44
  • 3Nie J F, Gao X, Zhu S M. Enhanced age hardening response and creep resistance of Mg-Gd alloys containing Zn[J]. Scripta Materialia, 2005, 53(9): 1049-1053.
  • 4Apps P J, Karimzadeh H, King J K. Precipitation reactions in magnesium-rare earth alloys containing yttrium, gadolinium or dysprosium[J]. Scripta Materialia, 2003, 48: 1023-1028.
  • 5Nie J F, Muddle B C. Characterisation of strengthening precipitate phases in a Mg-Y-Nd alloy[J]. Acta Materialia, 2000, 48(8): 1691-1703.
  • 6张新明,陈健美.高强耐热稀土镁合金:CN200610031169.9[P].2006-07-19.
  • 7Suzuki M, Sato H, Maruyama K. Creep behavior and deformation microstructures of Mg-Y alloys at 550 K[J]. Materials Science and Engineering A, 1998, 252(2): 248-255.
  • 8张新明,陈健美,邓运来,肖阳,蒋浩,邓桢桢.Mg-Gd-Y-(Mn,Zr)合金的显微组织和力学性能[J].中国有色金属学报,2006,16(2):219-227. 被引量:48
  • 9陈健美,张新明,邓运来,肖阳,熊创贤,蒋浩.镁合金熔炼的热力学[J].中南大学学报(自然科学版),2006,37(3):427-432. 被引量:10
  • 10马志新,张家振,李德富,张奎.铸态Mg-Gd-Y-Zr镁合金均匀化工艺研究[J].特种铸造及有色合金,2007,27(9):659-662. 被引量:34

二级参考文献49

共引文献159

同被引文献80

引证文献7

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部