摘要
合成了玻璃环氧底漆,讨论了附着力促进剂、树脂和固化剂种类及用量对涂料性能的影响。结果表明,以1.5%3–缩水甘油醚氧基丙基三甲氧基硅烷为附着力促进剂,以E-20环氧树脂为成膜物、腰果壳油改性酚醛胺为固化剂制成底漆,配合丙烯酸聚氨酯黑面漆,获得了高附着、耐水煮的玻璃漆。
An epoxy primer used on glass was synthesized, and the effects of categories and dosages of adhesion promoters, resins and curing agents were discussed. The results showed that a glass paint with high adhesion and boiling water resistance is obtained when acrylic polyurethane black top paint is combined with the primer prepared with 1.5% of 3-glycidoxypropyltrimethoxysilane as adhesion promoter, E-20 epoxy resin as film-forming material and cashew nut oil modified phenolic aldehyde amine as curing agent.