The performance of La2NiO4 perovskite catalysts,prepared using a citric acid complexation method,for the steam reforming of ethanol was studied.The catalysts were characterized by X-ray diffractometry(XRD),specific surface area measurements(BET),thermogravimetric analysis(TGA)and scanning electron microscopy(SEM).The experimental results show that the calcination temperature and the amount of citric acid(CA)have a significant influence on the characteristics of the catalysts and their catalytic activity.Among the catalysts tested,the La2NiO4 catalyst calcined at 700 ℃withn(La):n(Ni):n(CA)of 2:1:3 exhibits the best activity and excellent stability as well as very low coke formation.
The performance of La2NiO4 perovskite catalysts, prepared using a citric acid complexation method, for the steam reforming of ethanol was studied. The catalysts were characterized by X-ray diffractometry （XRD）, specific surface area measurements （BET）, thermogravimetric analysis （TGA） and scanning electron microscopy （SEM）. The experimental results show that the calcination temperature and thc amount of citric acid （CA） have a significant influence on the characteristics of the catalysts and their catalytic activity. Among the catalysts tested, the La2NiO4 catalyst calcined at 700 ℃ with n（La）：n（Ni）：n（CA） of 2：1：3 exhibits the best activity and excellent stability as well as very low coke formation.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2009年第6期1444-1449,共6页
Transactions of Nonferrous Metals Society of China