黄铜季裂研究

Research on Brass Stress Corrosion Cracking

本文主要详尽介绍了黄铜季裂产生的原因、原理。并用试验找到了防止黄铜季裂的方法,以便在生产中保证裂纹出现以前对工件进行热处理,保证产品质量,同时也为生产该类产品积累经验数据。

This article includes detailed descriptions of the cause and the principle of SCC （stress corrosion cracking）, and finds a way in experiments to prevent SCC. Work on heat treatment before the emergence of SCC in production, not only to guarantee product quality, but also for the production of these products from the accumulation of empirical data.