采用红外热成像仪测试了P92钢管道焊接温度场,并采用X射线衍射方法对P92管道焊接接头热处理前后的残余应力分布进行了测试。采用有限元方法对P92钢焊接温度场进行了计算和分析,并采用间接法用温度场结果计算残余应力场。分析比较了焊后热处理前后的焊接残余应力变化情况,证明焊后热处理对焊接残余应力具有一定的消除作用。
The welding temperature fields were measured using a thermal infrared imaging viewer, and the variation of the welding residual stress in the welded joint of P92 pipe before and after postweld heat treatment （PHT） were measured by the X- rays diffraction methods. The finite element methods （FEM） has been used to calculate and analyze the weld temperature field of P92 steel pipe, and the calculation results have been verified by comparing with the actual welding temperature fields. Subsequently, the FE analysis has been implemented to compute the welding residual stress using the indirect method. The variation of the welding residual stress was analyzed and compared before and after the PHT, and the result show that the PHT can effectively relieve part of residual stress.
出处
《压力容器》
北大核心
2009年第11期7-11,共5页
Pressure Vessel Technology
基金
国家自然科学基金青年基金项目(50805103)
天津市自然科学基金重点项目(08JCZDJC18100)
关键词
P92钢
热处理
温度场
残余应力测试
有限元方法
P92 steel
postweld heat treatmeht
temperature field
residual stress measurement
finite element method