摘要
利用透射电子显微镜和能谱,研究电子束焊接过程中Ti2AlNb基合金显微组织演变过程以及焊缝区组成、焊后热处理对接头显微组织的影响。结果表明:焊接过程中焊缝区Al元素损失较为严重,这有利于B2相的形成而不利于O相的形成,使得接头焊缝区主要由B2和α2两相组成;在随后的热处理过程中,焊缝区的B2相转变为β相和板条状的O相,使焊缝区由α2、O和β相组成。
The microstructure and composition of Ti2AlNb joints fabricated by electron beam welding technique were investigated by transmission electron microscopy （TEM） and energy dispersive spectrometer （EDS）. The effect of the composition of the welded zone and heat treatment after welding on the microstructure of the joint was also studied. Results showed that there was a great weight loss of Al element in the joint during welding, which was beneficial to the formation of B2 phase but O phase. The as-welded joint was composed of B2 and or2 phases, while the joint after heat treatment was of α2 ,O and β phases, which indicated that the following phase transformation of B2 to β and O occuned.