环境气氛对非晶Fe_(90)Zr_(10)合金条带表面状态的影响

THE EFFECT OF ENVIRONMENTAL ATMOSPHERES ON THE SURFACE STATE OF THE AMORPHOUS Fe_(90)Zr_(10) ALLOY RIBBON

分别在大气和氩气中制备了非晶Fe90Zr10条带采用AES及XPS，并结合氩离子原位溅射剥展，研究了气氛对条带自由侧及贴辊侧表面状态的影响结果表明，在大气中制备时，条带自由侧的Zr显著偏聚，贴辊侧发生了Fe的偏聚而在氩气中制备时，条带两侧表层的成分分布及氧化层厚度基本相同。

Amorphous Fe90Zr10 alloy ribbons were made in air and Ar atmosphere respectively.The effect of the atmospheres on the surface state of both the free and dull side of the amorphous alloy ribbon was studied by means of AES and XPS combined with in situ Ar ion bombardment etching.When the ribbon was formed in air, a notable difFerence of the depth profiIe of compositions and the thickness of oxide films between free and dull sides was found. The surface segregation of Zr was observed in the free side, while the dull side sudece was mainly composed of Fe oxides. When the ribbon was formed in the protective Ar atmosphere, there were similar depth profiles of the compositions and thickness of oxide films in free and dull side, and two sides were all covered with a thin layer of Fe oxides.