摘要
采用累计流量法对供应态Ti-6Al-4V合金进行了固态置氢,运用OM、XRD、TEM分析等方法研究了Ti-6Al-4V合金固态置氢后的微观组织状态及演变过程。结果表明:供应态Ti-6Al-4V合金的置氢量低于0.30%(质量分数,下同)时,置氢使得Ti-6Al-4V合金中的α相减少、β相增加;置氢量达到0.30%时,置氢Ti-6Al-4V合金中有δ氢化物(TiH2相)形成;β-Ti(H)共析转变生成α-Ti和δ氢化物时主要以切变方式进行;置氢Ti-6Al-4V合金的相变温度最多下降了180°C,与Ti-6Al-4V合金在置氢过程中的相体积比变化和共析转变有密切关系。
Hydrogenation of Ti-6Al-4V titanium alloys was carried out in a special furnace through the accumulated flux method, and OM, XRD and TEM techniques were used to investigate the microstructure evolution of the hydrogenated Ti-6AI-4V titanium alloy. The hydrogenation of the Ti-6Al-4V titanium alloy with the hydrogen content of 0.30 wt% makes the a phase fraction decrease compared with that of the as-received Ti-6Al-4V titanium alloy, but it makes the/~ phase fraction increase. The d hydride (Till2 phase) occurs in the hydrogenated Ti-6Al-4V titanium alloy when the hydrogen content is more than 0.3 wt%. The shear deformation is main pattern in the transformation processes from β-Ti(H) phase to α-Ti phase and δ hydride (TiH2 phase). The phase transformation temperature of the hydrogenated Ti-6Al-4Vtitanium alloy decreases by 180℃ compared with that of the as-received Ti-6Al-4V titanium alloy, and it is related to the phase fraction and phase transformation.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2010年第1期1-5,共5页
Rare Metal Materials and Engineering
基金
Supported by "973" Project
National Natural Science Foundation of China (50371068)
NPU-FFR-006