摘要
针对超临界锅炉管道的严重冲蚀磨损问题,采用高速电弧喷涂技术在20钢表面制取耐磨涂层,并研究其高温冲蚀磨损特性。采用场发射扫描电子显微镜和X射线能谱分析等方法探讨涂层的冲蚀磨损规律。结果表明,FeMnCr/Cr3C2涂层最大冲蚀率出现在冲击角60°附近,表现出半塑性冲蚀磨损特征;其耐高温冲蚀性与FeCrNi/Cr3C2涂层相近,明显优于20钢。
FeMnCr/Cr3C2 cored wire was developed for building up the erosion-resistant coatings of super-critical boiler pipes by means of High-Velocity Arc Spraying. The high-temperature erosion behaviors at different impact angles of FeMnCr/Cr3C2 coatings were studied and compared with those of FeCrNi/Cr3C2 coatings and 20 steel by optical microscopy, scanning electron microscopy and energy dispersion spectrum analysis. Results show that FeMnCr/Cr3C2 coatings have the maximum erosive rate when the impact angle is about 60° due to the semi-brittleness erosion mechanism for FeMnCr/CraC2 coatings. The erosion resistance of FeMnCr/Cr3C2 coatings is closed to that of FeCrNi/Cr3C2 coatings, and obviously better than that of 20 steel.