单边穿透裂纹楔块法疲劳止裂的有限元模拟
摘要
采用有限元方法,建立了二维裂纹—楔块接触问题的有限元模型。模拟计算了楔块与裂纹面之间的接触应力分布、楔块作用下裂纹张开位移、有效应力强度k因子等参数。分别讨论了加楔条件、楔块材料性质等因素对楔块法疲劳裂纹止裂效果的影响。上述初步分析结果可以为楔块法疲劳止裂技术的理论研究提供一定参考。
出处
《化工装备技术》
CAS
2010年第1期30-32,共3页
Chemical Equipment Technology
参考文献8
-
1银建中,马晓荣,李惠荣,王炎炎,秦红.疲劳裂纹楔块法止裂技术实验研究与模型化[J].化工装备技术,2008,29(6):25-33. 被引量:1
-
2Yin J Z, Wang Y Y, Ding X W. A new method of retarding fatigue crack growth on pressure vessels [J] . Journal of Materials Science & Technology, 2001, 17 : S73 - S76.
-
3银建中,王炎炎.压力容器人工楔块止裂加楔技术试验研究[J].石油化工设备,1998,27(4):5-7. 被引量:2
-
4银建中,王炎炎.压力容器人工楔块止裂技术的止裂机理研究[J].化工装备技术,1999,20(2):7-9. 被引量:2
-
5Shin C S, Cai C Q. Surface fatigue crack growth suppression in cylindrical rods by artificial infiltration [ J ] . International Journal of Fatigue 2008, 30 : 560 - 567.
-
6Shin C S, Cai C Q. Surface fatigue crack growth suppression in cylindrical rods by artificial infiltration [ J ] . International Journal of Fatigue. 2008, 30 : 560 - 567.
-
7Wang Y Y, Zho M X, Feng D Q. A study of retarding fatigue crack growth using an artificial wedge [ J ] . Fat. Fraet. Eng Mater. Struct, 1993, 16 (3): 363-376.
-
8葛庆麟.低应力下疲劳扩展门槛值△Kth.上海冶金,1980,2(4):73-78.
二级参考文献37
-
1银建中,王炎炎.压力容器及管道止裂技术研究与评价[J].化工装备技术,1996,17(6):31-33. 被引量:3
-
2银建中,王炎炎.表面裂纹疲劳止裂技术[J].材料研究学报,1997,11(2):173-177. 被引量:3
-
3杨玉昆 等.合成胶粘剂[M].北京:科技出版社,1980..
-
4Kitagawa H. A new method arresting fatigue crack growth by artificial wedge [ J] . Proc Int Fract Mech Engng Application India, 1979, 26-30:281 -293.
-
5Wang Y Y, Zho M X, Feng D Q. A study of retarding fatigue crack growth using an artificial wedge [ J ] . Fat Fract Engng Mater Struct, 1993, 16 (3) 363-376.
-
6Elber W. Fatigue crack closure under cyclic tension [ J] . Eng Fracture Mesh, 1981, 14:461 -465.
-
7白炎.楔块对16MnR疲劳裂纹迟滞效应的研究[D].大连:大连工学院,1987.
-
8Sharp P K, Clayton J Q, Clark G. Retardation and repair of fatigue cracks by adhesive infiltration [ J ] . Fatigue Fract Eng Mater Struct, 1997, 20 (4) : 605 -614.
-
9Shin C S, Huang K C, Li R Z. Artificial retardation of fatigue crack growth by the infiltration of cracks by foreign materials[J]. Fatigue & Fracture Eng Mater & Structure, 1998, 21:835 -846.
-
10Song P S, Sheu B C, Chou H H. Deposition of plating metals to improve crack growth life [ J ] . International Journal of Fatigue, 2001,23:259-270.
-
1银建中,马晓荣,李惠荣,王炎炎,秦红.疲劳裂纹楔块法止裂技术实验研究与模型化[J].化工装备技术,2008,29(6):25-33. 被引量:1
-
2银建中,王炎炎.表面裂纹疲劳止裂技术[J].材料研究学报,1997,11(2):173-177. 被引量:3
-
3孙建功.电磁热止裂对冷锻钢力学性能影响分析[J].锻压技术,2015,40(12):145-149.
-
4宋玉殿.ANSYS软件在结构焊接裂纹分析中的应用[J].焊接技术,2004,33(4):58-59. 被引量:3
-
5姜正连,刘相华,王国栋,孙浩.中厚板轧机的板形控制[J].轧钢,1996,13(4):17-19. 被引量:4
-
6李光耀.谈一道综合性习题的多种解法[J].牡丹江教育学院学报,2003(2):17-18.
-
7陈昌荣,黄维扬.冷胀孔单边穿透裂纹的应力强度因子计算方法[J].南京航空航天大学学报,1996,28(4):556-559.
-
8沈承金,秦熊浦.COD技术及300M钢腐蚀疲劳[J].理化检验(物理分册),1993,29(3):37-39. 被引量:1
-
9李春雨.用非等参边界元计算二维裂纹应力强度因子[J].石家庄铁道学院学报,1994,7(3):1-8. 被引量:1
-
10唐志文.未焊透对铝焊缝使用性能的影响[J].压力容器,2003,20(7):10-12. 被引量:1