摘要
采用提拉法生长了尺寸为φ(30~35)mm×80mm的掺钕钨酸钆钠[Nd:NaGd(WO4)2,Nd:NGW]晶体。生长Nd:NGW晶体的最佳工艺参数为:晶体的提拉速率为1~2mm/h,晶体转速为15~18r/min,冷却速率为10℃/h,液面上轴向温度梯度为0.7~1℃/mm。通过热重-差热分析(thermogravimetry-differential thermal analysis,TG-DTA),X射线衍射(X-ray diffraction,XRD)对晶体进行表征。测试了晶体的红外及Raman光谱,分析了晶体的振动模式,并将晶体振动光谱进行归属。由TG-DTA曲线得到晶体熔点为1251.7℃。XRD分析表明:晶体属于四方晶系、白钨矿结构、I41/a空间群,晶胞参数a=0.53213nm,c=1.13070nm。吸收光谱表明:Nd:NGW晶体在805nm附近有较强、较宽的吸收峰,吸收截面积为3.581×10-20cm2,适合于激光二极管泵浦。
Nd:NaGd(WO4)2 (Nd:NGW) single crystals with 30-35 mm in diameter and 80 mm long were grown by Czochralski method.The optimal growth parameters of the Nd:NGW crystal are:a pulling rates of 1-2 mm/h,a rotation rate of 15-18 r/min,a cooling speed of 10 ℃ /h and an axial temperature gradient on the solid-liquid interface of 0.7-1 ℃ /mm.The crystal was characterized by thermogravimetry-differential thermal analysis (TG-DTA) and X-ray diffraction (XRD).The infrared (IR) spectra and Raman spectra of the crystal were measured,and vibration frequencies of IR and Raman active modes for the crystal were assigned.TG-DTA curves indicate that the melting point of the Nd:NGW crystal is 1 251.7 ℃.The XRD analysis shows that the Nd:NGW crystal belongs to a tetragonal system with a scheelite-type structure and a space group I41/a,and the lattice parameters of the crystal are a=0.532 13 nm and c=1.130 70 nm.Absorption optical spectra of the Nd:NGW crystal show that there is better and wider absorb peak at about 805 nm,and the absorption cross-section of crystal sample is calculated to be 3.581 × 10-20cm2,which is suitable for laser diode pumping.
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2010年第2期177-182,共6页
Journal of The Chinese Ceramic Society
基金
总装备部(41312040801)资助项目
关键词
掺钕钨酸钆钠晶体
提拉法
红外光谱
RAMAN光谱
吸收光谱
neodymium doped gadolinium sodium tungstate crystal
Czochralski method
infrared spectra
Raman spectra
absorption spectrum