摘要
对管道堵塞疏通剂(简称疏通剂)进行了模拟应用及下水道常用配件的腐蚀和稳定性试验.结果显示:(1)在模拟应用试验中疏通剂与堵塞物加水反应30min后,管道内无堵塞残留物存在;(2)稳定性试验的测定数据经Van’tHof经验规则计算公式推算出疏通剂在25℃条件下储藏保质期至少在1年以上;(3)腐蚀试验(重量法)测定的PVC塑料管和铸铁管腐蚀前和经疏通剂腐蚀6h后所得数据经t-检验统计无显著性意义〔P(概率)>0.05〕.
The simulated appling, corrodentia of drain fittings and stability test of drain pipes block opener agent (opener agent) were studied. Data from determination showed: (1) No blocken-matter remained after putting opener agent and water in pipes for 30 min from simulated appling test; (2) The opener agent was in storege guarautee quality more than 1 year in the 25℃, date from determination of stability test with Van't Hoff experience requlations formula; (3) Date from PVC plastic and cast iron pipes both before and after corrodetia with adding the opener agent (lasted 6 hours) was not significant difference to weight method determination ( P >0.05).