研究了1420合金在不同热处理状态的拉伸性能和拉伸断口,并考察了合金的显微组织,分析了断裂机制.结果表明,合金在各种热处理状态呈稳定的穿晶韧性断裂,原因是δ粒子细小,晶内强度低,而且晶界没有材出平密相和无析出带,品界强度没有降低.
The tensile properties and the fracture surface of 1420 alloy in different aging states,are studied along with its ndcrostructure. And the fracture machanism is then presented. Severalconclusions are: 1420 alloy behaves stable transgranular fracture for its smaller δ' phase and noequilibrium in grain boundary which cause lower strength within grains.