余热处理技术通过优化控冷工艺控制系统,制定合理的穿水冷却操作规程,生产符合国家标准及英、美、德等先进国家标准的高强度等级建筑钢筋。研究表明,钢筋表面发生淬火、回火转变,根据强度等级的不同,显微组织为回火马氏体或者回火索氏体,芯部为铁素体加珠光体或者铁素体加索氏体、贝氏体等,钢筋具有高强度和良好塑性的理想配合。
The controlling system of remained heat treatment technology is optimized, and the proper water cooling regulations are established. The high quality and high strength reinforced bars are produced according to GB, BS, ASTM, DIN, etc. The investigations reveal that quenching-tempering transformation occurs at the surface layer of the reinforced bar produced by remained heat treatment, and the microstructure of the layer is consist of tempered martensite or sorbite. There are ferrite and pearlite, or ferrite and sorbite, bainite, and so on at the center area. The bars possess ideal strength and plastic properties. The strength of the bar will decrease observably by welded . The bar is fit for non-weld joint.
出处
《山西冶金》
CAS
2010年第1期21-23,共3页
Shanxi Metallurgy
关键词
余热
淬火
钢筋
马氏体
性能
remained heat, quenching, reinforced bar, martensite, property