Through changing soaking temperature and soaking time,austenite grain growth behavior of X80 pipeline steel under different heating conditions was studied. Relationships of average grain size to soaking temperature and time were obtained respectively. The results show that the prior austenite grains grow with the increase of soaking temperature and time. When soaking temperature is lower than 1180℃,austenite grain size and growth rate are small; when it higher than 1200℃,austenite grains grow rapidly and abnormal grain growth appears. For soaking at 1180℃,austenite grain growth rate is initially high and then decreases when soaking time exceeds 1h.
在Through changing soaking temperature and soaking time, austenite grain growth behavior of X80 pipeline steel under different heating conditions was studied. Relationships of average grain size to soaking temperature and time were obtained respectively. The results show that the prior austenite grains grow with the increase of soaking temperature and time. When soaking temperature is lower than 1 180 ℃, austenite grain size and growth rate are small; when it higher than 1 200 ℃, austenite grains grow rapidly and abnormal grain growth appears. For soaking at 1 180 ℃, austenite grain growth rate is initially high and then decreases when soaking time exceeds 1 h.
基金
Item Sponsored by National Key Technology Research and Development Program of China (2006BAE03A15)
Natural Science Foundation of Yunnan Province of China (2006E0017Q)