摘要
波纹管补偿器的失效主要有腐蚀泄漏和失稳两种形式。通过一生产实例对高氯离子工作环境下不锈钢波纹管补偿器的腐蚀开裂原因进行分析,并提出了改进措施,确保了波管补偿器工作的安全可靠性。
Bellows compensator failure was mainly due to corrosion Leaks and instability. Through the production instance, it analyzed the causes of corrosion cracking of stainless steel bellows compensator in high chloride ion enviroment. And proposed measures for improvement. Even more to ensure the seaurity and reliability of bellows compensator work.
出处
《盐业与化工》
CAS
2010年第2期52-54,共3页
Jounral of Salt and Chemical Industry
关键词
波纹管补偿器
腐蚀开裂
原因
bellows compensator
corrosion cracking
reason