Relationship between the geometric features of carbon steel cavitation erosion debris and the cavitation erosion stages 被引量:1

Relationship between the geometric features of carbon steel cavitation erosion debris and the cavitation erosion stages
原文传递
导出
摘要 The debris produced in vibration cavitation tests of three kinds of carbon steel were collected.Their geometric features were analyzed quantitatively and observed respectively by a profilometer and a scanning electronic microscope(SEM) with reference to the investigation of the cavitation damaged surface by SEM and X-ray diffraction(XRD) .It was found that among the debris produced in all cavitation erosion stages,more than 45%were platelets because of the occurrence of dislocation and cleavage fracture,and only less than 25%were strands.The number of granule was small in the first cavitation erosion stage and increased rapidly to the number comparable with that of platelets in the next stage,and then reduced in the third stage.The sphericity values of the debris varied in accordance with the stages of cavitation damage,which were 0.3―0.4 in the incubation stage,0.5―0.7 in the acceleration stage and not less than 0.5 in the maximum rate stage,although a slight decrease occurred in the third stage. The debris produced in vibration cavitation tests of three kinds of carbon steel were collected. Their geometric features were ana- lyzed quantitatively and observed respectively by a profilometer and a scanning electronic microscope (SEM) with reference to the investigation of the cavitation damaged surface by SEM and X-ray diffraction (XRD). It was found that among the debris produced in all cavitation erosion stages, more than 45% were platelets because of the occurrence of dislocation and eleavage fracture, and only less than 25% were strands. The number of granule was small in the first cavitation erosion stage and increased rapidly to the number comparable with that of platelets in the next stage, mad then reduced in the third stage. The sphericity values of the debris varied in accordance with the stages of cavitation damage, which were 0.3--0.4 in the incubation stage, 0.5--0.7 in the acceleration stage and not less than 0.5 in the maximum rate stage, although a slight decrease occurred in the third stage.
出处 《Chinese Science Bulletin》 SCIE EI CAS 2010年第7期670-676,共7页
基金 supported by the National Basic Research Program of China(Grant No.2007CB707702) Key Project of State Key Laboratory of Tribology of China
关键词 几何特征 碳素钢 空蚀 扫描电子显微镜 X射线衍射仪 扫描电镜 血小板数 振动试验 carbon steel, cavitation erosion stage, debris, geometric feature
  • 相关文献

参考文献1

二级参考文献3

  • 1易家训著.流体力学[M].高等教育出版社,1997..
  • 2杨志伊等.旋转式铁谱仪在设备工况监测中新的突破[J].武汉交通大学报,1994,18.
  • 3龚文麟 徐承和.近代电磁理论[M].北京:北京大学出版社,1995..

共引文献1

同被引文献23

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部