摘要
以甲基丙烯酸锌(ZDMA)/白炭黑填充氢化丁腈橡胶(HNBR),研究ZDMA/白炭黑并用比、硫化剂DCP用量及硫化时间对HNBR硫化胶结构和性能的影响。结果表明,在填料总量不变的前提下,随着白炭黑用量的增大,ZDMA/白炭黑填充HNBR硫化胶拉伸强度和压缩永久变形先减小后增大,填料分散性下降;随着硫化剂DCP用量的增大,ZDMA/白炭黑填充HNBR硫化胶物理性能和动态性能提高,填料分散性变好。当ZDMA/白炭黑并用比为10/30、硫化剂DCP用量为5~6份、一段硫化条件为160℃×45min、二段硫化条件为150℃×(9~12)h时,ZDMA/白炭黑填充HNBR硫化胶综合性能较好。
Hydrogenated nitrile rubber(HNBR)was filled with zinc dimethacrylate(ZDMA)/silica,and the effects of ZDMA/silica blending ratio,the addition level of vulcanizator dicumyl peroxide(DCP)and curing time on the structure and properties of HNBR vulcanizates were investigated.The results showed that,the tensile strength and compression set of ZDMA/silica filled HNBR vulcanizate were decreased at first and then increased,the filler dispersibility was declined as the addition level of silica increased while filler amount was constant;the physical properties and dynamic properties of ZDMA/silica filled HNBR vulcanizates were improved,and filler dispersibility was enhanced when the addition level of DCP was increased.It was found that excellent comprehensive properties of ZDMA/silica filled HNBR vulcanizate could be obtained when the blending ratio of ZDMA/silica was 10/30,the addition level of DCP was 5~6 phr,and the first-stage vulcanization condition was 160 ℃×45 min and the second-stage vulcanization condition was 150 ℃×(9~12)h.
出处
《橡胶工业》
CAS
北大核心
2010年第2期69-75,共7页
China Rubber Industry
关键词
氢化丁腈橡胶
甲基丙烯酸锌
白炭黑
物理性能
动态性能
分散性
hydrogenated nitrile rubber
zinc dimethacrylate
silica
physical property
dynamic property
dispersibility