The performance of an organic photovoltaic （OPV） cell based on copper phthatocyanine CuPc/C60 with a tris- （8-hydroxyquinolinato） aluminum （Alq3） buffer layer has been investigated. It was found that the power conversion efficiency of the device was 1.51% under illumination with an intensity of 100 mW/cm^2, which was limited by a squareroot dependence of the photocurrent on voltage. The photocurrent optical power density characteristics showed that the OPV cell had a significant space-charge limited photocurrent with a varied saturation voltage and a three quarters power dependence on optical power density. Also, the absorption spectrum was measured by a spectrophotometer, and the results showed that the additional Alq3 layer has a minor effect on photocurrent generation.
The performance of an organic photovoltaic （OPV） cell based on copper phthatocyanine CuPc/C60 with a tris- （8-hydroxyquinolinato） aluminum （Alq3） buffer layer has been investigated. It was found that the power conversion efficiency of the device was 1.51% under illumination with an intensity of 100 mW/cm^2, which was limited by a squareroot dependence of the photocurrent on voltage. The photocurrent optical power density characteristics showed that the OPV cell had a significant space-charge limited photocurrent with a varied saturation voltage and a three quarters power dependence on optical power density. Also, the absorption spectrum was measured by a spectrophotometer, and the results showed that the additional Alq3 layer has a minor effect on photocurrent generation.
基金
Project supported by the National Natural Science Foundation of China (NSFC) (Grant Nos. 60736005 and 60425101-1)
the Foundation for Innovative Research Groups of the NSFC (Grant No. 60721001),Provincial Project (Grant No. 9140A02060609DZ0208)
Program for New Century Excellent Talents in University (Grant No. NCET-06-0812),SRF for ROCS,SEM (Grant No. GGRYJJ08-05)
Young Excellent Project of Sichuan Province (Grant No. 09ZQ026-074)