摘要
1J50软磁合金的性能主要是通过H2热处理获得的,在1130℃和H2气氛保护下对冷轧态1J50软磁合金进行了热处理。运用MATS-2010SA软磁测试仪对处理前后1J50软磁合金的磁性能进行了检测,运用金相显微镜、XRD等手段对处理前后1J50软磁合金的组织结构进行了分析。结果表明,通过H2热处理,1J50软磁合金的矫顽力显著降低,起始磁导率和最大磁导率提高;组织结构发生明显变化,冷轧态1J50软磁合金组织为孪晶奥氏体,平均晶粒尺寸为200μm,处理过后,晶粒显著长大,平均晶粒尺寸为100μm;由于在600℃时采取了快冷,处理后1J50软磁合金中未出现大量FeNi相和FeNi3相。
In this paper,H2 protection heat treatment at 1130℃ was carried out to enhance the performance of 1J50(Fe-50%Ni) alloy.MATS-2010SA soft magnetic advice was used to test the soft magnetic performance of pretreated and astreated 1J50 alloy and the microscopy and XRD was used to show the microstructure of pretreated and astreated 1J50 alloy.Results showed that after H2 protection heat treatment the Hc of 1J50 alloy reduced sharply while the Bs rised.The microstructure of pretreated and astreated 1J50 alloy was austinite,but the grain size of astreated 1J50 alloy was more than two times of pretreated.XRD revealed that after heat treatment there was no FeNi and FeNi3 phase becaused of rapid cooling.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2010年第3期463-465,共3页
Journal of Functional Materials
基金
中国航天科技集团中国运载火箭研究院资助项目(2008033)
关键词
H2热处理
1J50
组织结构
性能
H2 protection heat treatment
1J50 alloy
microstructure
performance