摘要
LaFe11.4Si1.6By(y=0、0.1、0.2、0.3、0.4和0.5)系列化合物,通过添加少量的B后,可以明显的缩短退火时间。晶格常数随着B含量的增加先减小后增大。该系列化合物的热滞很小,B的添加对其热滞几乎没有影响。在外加磁场变化为0～1.5T时,等温磁熵变的最大值从19.1J/(kg.K)(y=0)逐渐下降到7.1J/(kg.K)(y=0.5)。该系列化合物在B含量较低时,处于居里温度(Tc)之上,存在比较明显的场致变磁转变特性。随着B含量增加到0.5时,场致变磁转变特性明显减弱。
The annealing time of LaFe11.4Si1.6By（y=0,0.1,0.2,0.3,0.4 and 0.5） compounds can be reduced obviously by introducing interstitial atom B.The lattice parameter slightly decreased first and then increases with increasing B content.It can be seen that the small thermal hysteresis between heating and cooling curves for these compounds,but the thermal hysteresis is not affected by B addition.The maximal magnetic entropy change decreases from 19.1 to 7.1 J/（kg·K） by changing y from 0 to 0.5 for a magnetic field change from 0 to 1.5T.It is obvious that the itinerant electron metamagnetic（IEM） transition for low B content above the Curie temperature.The IEM transition disappears when y increase to 0.5.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2010年第3期515-519,共5页
Journal of Functional Materials
基金
国家自然科学基金资助项目(50661004)
内蒙古科技计划资助项目(20070402)
黄山学院自然科学资助项目(2008xkjq010)
关键词
磁熵变
磁热效应
金属间化合物
变磁转变
稀土
magnetocaloric effect
magnetic entropy change
Intermetallic compounds
itinerant electron metamagnetic transition
rare earths