摘要
用TG-DTG技术,对二维聚硫杂酞青铜(PCuS8Pc)的非等温热解动力学进行了研究.结果表明,在静态氮气气氛和升温速率为20℃·min-1时,PCuS8Pc的热分解为3步,其热分解机制均受随机核化和生长(Am)控制.各步分解的活化能分别为49.80,54.03和162.33kJ·mol-1,指前因子分别为1.19×107,1.44×104和1.10×1010min-1.
By mean of TG DTG,the kinetics of non isothermal thermal degradation of two dimensional poly (copper octathiotetraazaporphyrin)(PCuS 8Pc) is studied in a static nitrogen atmosphere at heating rate of 20 ℃·min -1 .The result shows the decomposition of PCuS 8Pc takes place in three stages.The models of the thermal decomposition of PCuS 8Pc is dominated by random nucleation and subsequent growth process ( A m).It was found that m is 0.75, 0.70 and 0.45 . The activation energy ( E a ) is 49.80, 54.03 and 162.33 kJ·mol -1 , the pre exponetial factor ( A ) is 1.19×10 7, 1.44×10 4 and 1.10×10 10 min -1 for each stage respectively.
出处
《中南民族学院学报(自然科学版)》
1998年第4期1-5,共5页
Journal of South-Central University for Nationalities(Natural Sciences)
基金
国家自然科学基金
关键词
动力学
聚硫杂酞青铜
热分解
非等温热解
kinetics
two dimesional poly (copper octathiotetraazaporphyrin)
thermal decomposition
reaction mechanism