A series of lanthanum doped meosoporous MCM-41 （LaxM41, x is Si/La molar ratio） was prepared by sol-gel method. The surface structure of the materials was investigated with X-ray diffraction and N2 adsorption/desorption technique. The content of La in the materials was determined by ICE It was found that the La content of La25M41, La50M41 and La100M41 was 7.53%, 3.89% and 2.32%, respectively. The phosphate adsorption capacities increased with increasing amount of La incorporation. With 0.40 g La25M41 99.7% phosphate could be removed. The effects of Si/La molar ratio, LaxM41 dose, pH, initial concentration of phosphate solution, co-ions on phosphate adsorption were also evaluated. The phosphate adsorption kinetics of LaxM41 could be well-described by the pseudo second-order model, and Langmuir isotherm fit equilibrium data much better than the Freundlich isotherm.
A series of lanthanum doped meosoporous MCM-41 （LaxM41, x is Si/La molar ratio） was prepared by sol-gel method. The surface structure of the materials was investigated with X-ray diffraction and N2 adsorption/desorption technique. The content of La in the materials was determined by ICE It was found that the La content of La25M41, La50M41 and La100M41 was 7.53%, 3.89% and 2.32%, respectively. The phosphate adsorption capacities increased with increasing amount of La incorporation. With 0.40 g La25M41 99.7% phosphate could be removed. The effects of Si/La molar ratio, LaxM41 dose, pH, initial concentration of phosphate solution, co-ions on phosphate adsorption were also evaluated. The phosphate adsorption kinetics of LaxM41 could be well-described by the pseudo second-order model, and Langmuir isotherm fit equilibrium data much better than the Freundlich isotherm.
基金
supported by the National Major Research Plan for Water Pollution Control and Treatment of China (No.2008ZX07101-015)