The complex fluoride, KNiF3, with perovskite structure was synthesized by refluxing KF and Ni（NO3）2·6H20 in ethanediol. The samples were characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM）, X-ray photoelectron spectroscopy（XPS）, and ultraviolet-visible diffuse reflectance speetroseopy（UV-Vis DRS）. The results indicate that the mean diameter of KNiF3 particles is about 30-60 nm and the oxygen content in the samples is ≤5%. The prepared KNiF3 shows obvious absorption peaks at 400-830 nm.
The complex fluoride, KNiF3, with perovskite structure was synthesized by refluxing KF and Ni（NO3）2·6H20 in ethanediol. The samples were characterized by X-ray diffraction（XRD）, transmission electron microscopy（TEM）, X-ray photoelectron spectroscopy（XPS）, and ultraviolet-visible diffuse reflectance speetroseopy（UV-Vis DRS）. The results indicate that the mean diameter of KNiF3 particles is about 30-60 nm and the oxygen content in the samples is ≤5%. The prepared KNiF3 shows obvious absorption peaks at 400-830 nm.
基金
Supported by the National Natural Science Foundation of China(No.20671069)