合成了1种含硼及钡的油溶性化合物——正辛氧基硼酸钡(BaOB),将其作为润滑油抗磨减摩添加剂,采用四球摩擦磨损试验机评价了其摩擦学性能。结果表明,在菜籽油(RO)中加入BaOB后,其承载能力得到明显提高,最大增幅超过80%,钢球磨斑直径和摩擦系数均明显降低,且588N时的摩擦系数较392 N时的更低;扫描电子显微镜证实钢球磨斑表面有沉积物。从SEM/EDS和XPS分析摩擦副表面发现,摩擦副表面有B、Ba、Fe、Cr元素,在摩擦过程中正辛氧基硼酸钡发生了摩擦化学反应,并在摩擦副表面生成了BaO、B2O3和FeB抗磨减摩膜,从而改善了菜籽油的摩擦磨损性能。
Oil-soluble abrium octoxyborate （BaOB） was synthesized. Its tribological properties as lubricating oil additive for rapeseed oil （RO） were evaluated by using four-ball machine. The worn steel surface of steel ball was investigated with SEM/EDS and XPS. The results indicated that the wear resistance and load-carrying capability of RO with BaOB added were increased, the max load-carrying capability increased by 80%. The friction coefficient of RO was decreased by the addition of BaOB, and the friction coefficient under 588 N was lower than that under 392 N. the tribochemical reaction occurred in the friction progress, generating a protective film containing BaO, B2O3 and FeB on the worn steel surface, which contributes to improving the anti-wear and extreme pressure properties of the rapeseed oil.
出处
《石油学报（石油加工）》
EI
CAS
CSCD
北大核心
2010年第2期264-267,共4页
Acta Petrolei Sinica(Petroleum Processing Section)
基金
湖南省教育厅项目(04C059)
总后勤部军需物资油料部(需物油科[2006]357号)
湖南省科技计划项目(06FJ4112)资助
关键词
正辛氧基硼酸钡
菜籽油
摩擦学性能
润滑机理
barium octoxyborate
rapeseed oil
tribological properties
lubrication mechanism